* Titanium Grade 17 *
Chemical composition (weight %) (Maximum values unless range is shown)
O
N
C
H
Fe
A1
V
Ni
Mo
Pd
Residuals
0.18
0.03
0.08
0.015
0.2
0.04-0.08
0.4


Corrosion-resistant titanium alloy offering outstanding resistance to general and localized crevice corrosion in
a wide range of oxidizing and reducing acid environments oncluding chlorides. Has a good balance of
moderate strength, reasonable ductility and excellent weldability.
 
Mechanical properties at room temperature
 
Minimum values
Typical values
Yield Strength
275 MPa
350 MPa
Ultimate Strength
345 MPa
485 MPa
Elongation in 50 mm, A5
20%
28%
Reduction in Area
%
%
Hardness
150 HV
Modulus of elasticity
103 GPa
Charpy V-Notch Impact
40-85 J