* Titanium Grade 2 *
Chemical composition (weight %) (Maximum values unless range is shown)
O
N
C
H
Fe
A1
V
Ni
Mo
Others
Residuals
0.25
0.03
0.08
0.015
0.3
0.4


Grade 2 is the most widely used titanium allow in all product forms for industrial service, offering an excellent
balance of moderate strength and reasonable ductility. Highly corrosion-resistant in highly oxidizing and
mildly reducing environments, including chlorides.
 
Mechanical properties at room temperature
 
Minimum values
Typical values
Yield Strength
275 MPa
350-450 MPa
Ultimate Strength
345 MPa
485 MPa
Elongation in 50 mm, A5
20%
28%
Reduction in Area
30%
55%
Hardness
160-200 HV
Modulus of elasticity
103 GPa
Charpy V-Notch Impact
40-82 J