* Titanium Grade 28* |
Chemical composition (weight %) (Maximum values unless range is shown) |
O |
N |
C |
H |
Fe |
A1 |
V |
Ni |
Mo |
Ru |
Residuals |
0.15 |
0.03 |
0.08 |
0.015 |
0.25 |
2.5-3.5 |
2.0-3.0 |
|
|
0.08-0.14 |
0.4 |
|
|
|
Grade 9 with Ruthenium for improved corrosion resistance.
|
| |
Mechanical properties at room temperature |
| |
Minimum values |
Typical values |
|
Yield Strength |
485 MPa |
610 MPa |
Ultimate Strength |
620 MPa |
740 MPa |
Elongation in 50 mm, A5 |
15% |
17% |
Reduction in Area |
25% |
% |
Hardnes |
|
260-320 HV |
Modulus of elasticity |
|
107 GPa |
Charpy V-Notch Impact |
|
48-102 J |
|
|
| |