* Titanium Grade 29*
Chemical composition (weight %) (Maximum values unless range is shown)
O
N
C
H
Fe
A1
V
Ni
Mo
Ru
Residuals
0.13
0.03
0.08
0.0125
0.25
5.5-6.5
3.5-4.5
0.08-0.14
0.4


Grade 23 with Ruthenium for improved corrosion resistance. High crevice corrosion temperature, improved stress corrosion resistance compared to Grade 5.
 
Mechanical properties at room temperature
 
Minimum values
Typical values
Yield Strength
790(760) MPa
825 MPa
Ultimate Strength
860(825) MPa
895 MPa
Elongation in 50 mm, A5
10 (7.5)%
15%
Reduction in Area
25 (15)%
%
Hardnes
350HV
Modulus of elasticity
114 GPa
Charpy V-Notch Impact
24-40 J