* Titanium Grade 3 *
Chemical composition (weight %) (Maximum values unless range is shown)
O
N
C
H
Fe
A1
V
Ni
Mo
Others
Residuals
0.35
0.05
0.08
0.015
0.30
0.4


Grade 2 is the most widely used titanium allow in all product forms for industrial service, offering an excellent
balance of moderate strength and reasonable ductility. Highly corrosion-resistant in highly oxidizing and
mildly reducing environments, including chlorides.
 
Mechanical properties at room temperature
 
Minimum values
Typical values
Yield Strength
380 MPa
460 MPa
Ultimate Strength
450 MPa
595 MPa
Elongation in 50 mm, A5
18%
25%
Reduction in Area
30%
%
Hardness
180-220 HV
Modulus of elasticity
103 GPa
Charpy V-Notch Impact
24 - 48 J